Twist Drill

External cooling

Internal cooling

φ12

φ14

φ16

φ18

Mild steel, long chip

(＜125HB)

120-80-50

140-100-60

0.18-0.28-0.40

0.22-0.32-0.45

0.22-0.32-0.45

0.25-0.38-0.50

0.25-0.38-0.50

Mild steel, short chip, free cutting steel(＜25HRC)

120-75-50

140-100-60

0.18-0.28-0.40

0.22-0.32-0.45

0.22-0.32-0.45

0.25-0.38-0.50

0.25-0.38-0.50

High and medium carbon steel

(＜35HRC)

120-70-45

120-80-60

0.18-0.28-0.38

0.22-0.32-0.45

0.22-0.32-0.45

0.25-0.38-0.50

0.25-0.38-0.50

Alloy steel, tool steel

(＜35-48HRC)

100-70-45

110-50-60

0.15-0.23-0.34

0.18-0.25-0.38

0.18-0.25-0.38

0.25-0.38-0.50

0.20-0.30-0.40

Alloy steel, tool steel

(＜35-48HRC)

80-60-35

90-60-35

0.11-0.19-0.30

0.12-0.22-0.32

0.12-0.22-0.32

0.20-0.30-0.40

0.14-0.24-0.34

PH, ferrite and  martensite steel

(＜35HRC)

70-50-30

90-60-30

0.10-0.18-0.28

0.12-0.20-0.30

0.12-0.20-0.30

0.14-0.24-0.32

0.14-0.24-0.32

High strength PH, ferrite and martensite steel(35-48HRC)

70-45-25

80-50-30

0.10-0.18-0.28

0.12-0.20-0.30

0.12-0.20-0.30

0.14-0.24-0.32

0.14-0.24-0.32

Grey cast iron

(＜32HRC)

140-100-60

160-120-60

0.25-0.33-0.45

0.28-0.36-0.48

0.30-0.40-0.50

0.32-0.42-0.52

0.35-0.45-0.55

Alloy cast iron, nodular cast iron

(＜28HRC)

120-80-60

140-100-60

0.22-0.30-0.42

0.24-0.33-0.45

0.25-0.35-0.48

0.28-0.38-0.48

0.30-0.40-0.50

Difficult cutting alloy cast iron, nodular cast iron (＜45HRC)

100-70-50

100-80-50

0.16-0.22-0.28

0.18-0.24-0.30

0.20-0.26-0.32

0.22-0.28-0.34

0.23-0.28-0.35